Iron separator common faults and solutions

Iron separators and flotation machines are the most common mineral processing line machines, and their importance cannot be underestimated. Therefore, failures should be solved in time. In the course of their use, what common faults will occur, how to solve it when we meet again, let Let's discuss this issue:

1. When you use the iron slag for the iron remover to enter the obstacle, the lighter should track the drum skin, and the heavy one should be cut off by the drum or the drum skin. When this phenomenon occurs, stop the obstacle immediately. Usually, the iron remover should be prohibited from using the manufacturer's bolts, nuts, wire and other metal objects into the iron remover.

2. When you use the magnetic separation tube, disconnect it at the ferromagnetic slag block, there is a kaka sound in the cylinder. In severe cases, when the drum skin is cut off, the maintenance should be stopped immediately. To prevent the magnet block from falling off again, you can use the thin copper to make the live magnetic system during repair.

3, the use of semi-reverse flow ditch bottom mouth sometimes caused by calcium and blockage of the nozzle in the deposit or work blockage, suspect this problem should stop checking. Sometimes the nozzle is not blocked, but somewhere it is working due to the congested work space. The fault phenomenon is that the drum skin is not concentrated and can be used for high pressure water block blockage.

4. When you use iron slag grinding iron remover, such as semi-reverse flow intermediate layer or tailings tube leakage mill, the original ore will short circuit into the tailings, and the tailings grade will rise if there is sudden high tailings grade and high. Phenomenon can be suspected to be a tank leakage solution.

5. If your iron ore slag magnetic separator has been used for many years, the grade of tailings is gradually rising when the ore properties are unchanged. Perhaps because of the decrease in magnetic properties, the strength of the magnetic field is reduced. When magnetite slag magnetic separation airport strength measurement, if the magnetic field strength decreases too much, it should be carried out at the time of magnetization.

6, if the iron remover is a mechanical failure of iron slag, such as gear wear, loose screws and misalignment, motor failure, etc., should promptly find timely maintenance.