Drying equipment debugging: (1) Adjust the inlet temperature of spray drying equipment 220±20℃, the outlet temperature 110±10℃, the feeding speed 80Kg/hr, and then start charging spray drying, get dry materials, and then remove iron through PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC. (2) The solid content can be adjusted to 15%~30% according to the spray particle size.

PTMS magnetic separator

The pressure of hydraulic press was adjusted to 150 tons and 175 tons respectively, and the materials with good iron removal by PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC were loaded into the mold with spray drying, and the pressure was kept for a certain time, and compacted into blocks. Load the sagger into the push plate furnace. At the same time, several groups of bulk samples were placed and compared with the material pressed into blocks.

how to separate two magnets？

Push plate furnace sintering, the use of LITHIUM battery roller furnace, PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC iron removal after drying materials for sintering, the market advanced roller furnace adopts advanced infrared technology and advanced furnace materials, improve the thermal efficiency of equipment; Adopt advanced temperature control technology to ensure the accuracy of temperature control; Using mature furnace body design technology to ensure the uniformity of furnace temperature; Scientific and reasonable transmission mechanism is adopted to ensure smooth and stable operation of the push plate. The sagger was pushed into the push plate furnace for 4-6 hours according to the heating period of 300-550℃. 750℃ constant temperature section 8-10 hours; Cooling section 6-8 hours, discharge.
Contact: DELLA
Mob: +86-13929907491
sales@powtechina.com