The Fe2O3 content of kaolin decreased by 50% after the high gradient of PTMS Electromagnetic Separator
published date: 2024/7/6

magnetic separator price

High efficiency iron removal process steps of kaolin: simply purify the kaolin raw ore, PTMS Electromagnetic Separator get the magnetic separation raw material; the magnetic separation raw material is prepared into a mixed slurry with solid content of 15%, and then the magnetic separation raw material mass is 2%. After sodium hexametaphosphate slurry stirring for 20min, 325 mesh wet screen;

PTMS magnetic separation


Using the slurry for high gradient PTMS Electromagnetic Separator, control the magnetic field strength of the high gradient magnetic separator is 1.0T and the slurry flow rate is 1.0 cm/s. Select the slurry through the high gradient magnetic separation machine, and the amount of alum is 6% of the quality of concentrate slurry, after adding the concentrate slurry to alum flocculation, filtration, drying, packaging, get the magnetic concentrate;

how to separate two magnets?


The resulting magnetic concentrate concentrate was calcined to obtain calcined kaolin and calcined for whiteness test. The whiteness of calcined kaolin (magnetic concentrate) was tested, the whitening was 91.3%, the Fe2O3 content was reduced from 1.27% before PTMS Electromagnetic Separator to 0.405%, the iron removal rate was 68%, and the content of Ti02 content was reduced from 0.29% to 0.253%.
Contact: DELLA
Mob: +86-13929907491
sales@powtechina.com

SILICA SAND PTMS magnetic separation 20240706

Share to:

Powtech Machinery Company produce magnetic separator, Industrial Magnetic Separators, Industrial magnetic separation equipments,Magnetic Equipment,Permanent Suspension Magnet,Vibrating Equipment