For the firing whiteness test of PTMS Electromagnetic Separator kaolin concentrate, the firing whiteness was 93.6%, the Fe2O3 content was reduced from 1.27% before magnetic separation to 0.39%, the iron removal rate was 69.0%, and the TiO2 content was reduced from 0.29% to 0.092%. How to adjust the efficient iron removal process of kaolin?

PTMS magnetic separation

 
The magnetic separation material is prepared into a mixed slurry of 15%, and then the magnetic separation material is 5%. Stir sodium hexadaphosphite for 20min, pass 325 mesh wet sieve; sieve the slurry for high gradient magnetic separation,

what is magnetic separation in Feldspar？

 
The magnetic field strength of high gradient PTMS Electromagnetic Separator is 1.4T, and the slurry flow rate is 1.0 cm/s. Using the slurry for magnetic separation, the amount of alum is 5% of the quality of concentrate slurry, dried and packed, and the concentrate is calcination after the calcination.